Modern concrete technology supplements the traditional components of aggregate, cement and water with concrete additives and admixtures. In this way, optimized properties can be achieved for different areas of application, for example in terms of strength and temperature development. cyment is used as a type II additive (pozzolanic or latent hydraulic additives) in accordance with EN 206 and can thus be counted towards the cement content. The climate-friendly advantage? The significantly optimized life cycle assessment of concrete.
cyment L 100 is applicable as a type II concrete additive according to EN 206 and improves the properties of fresh concrete, the properties of concrete during hardening (reduction of hydration heat) and the properties of hardened concrete (dense pore structure, high final strength and durability). cyment L 100 is generally suitable for all applications in civil engineering, in particular for use in massive elements, in water-impermeable constructions and in base layers stabilized with binders. In order to ensure the durability of the concrete produced with cyment L, sufficient curing (e.g. by keeping it moist, covering it with foil, spraying on liquid curing agents or leaving it in the formwork) of the concrete must be ensured. The curing of young concrete serves to protect the surface from drying out prematurely, from cooling or heating too much and from rapid temperature changes.
Properties according to valid ETA
Guide values
Requirements according to ETA 23/0294
Activity index [%, 28 days]
90
≥ 75 %
Activity index [%, 90 days]
100
≥ 85 %
Density [kg/dm³]
3,0
2,9-3,3
Grinding fineness (Blaine) [m²/kg]
670
≥ 400
cyment L 500 is applicable as a type II concrete additive for rapid hardening concretes according to EN 206 and improves the properties of fresh concrete, the properties of concrete during hardening and the properties of hardened concrete (dense pore structure, high final strength and durability). cyment L 500 is generally suitable for the precast industry and in particular for components that require rapid strength development. In order to ensure the durability of the concrete produced with cyment L, sufficient curing (e.g. by keeping it moist, covering it with foil, spraying on liquid curing agents or leaving it in the formwork) of the concrete must be ensured. The curing of young concrete serves to protect the surface from drying out prematurely, from cooling or heating too much and from rapid temperature changes.
Properties according to valid ETA
Guide values
Requirements according to ETA 23/0294
Activity index [%, 28 days]
90
≥ 75 %
Activity index [%, 90 days]
100
≥ 85 %
Density [kg/dm³]
3,0
2,9-3,3
Grinding fineness (Blaine) [m²/kg]
670
≥ 400
Whether ready-mix concrete, site concrete, precast elements, mortar, concrete blocks, stabilizations: As a climate-friendly binder, the versatile Type II admixture cyment provides the ideal solution forCO2-reduced concrete with properties perfected to meet specific requirements. For sustainable construction with an optimal eco-balance.
The result: a concrete admixture whosecarbon footprint shows how to do it right. Where it can be used? On any construction site.